| 8kg ua |
55# |
C: {{0}}.52-0.60, Mn: 0.50-0.80, Si: 0. 17-0.37, S: Tsawg dua lossis sib npaug rau 0.035, P: Tsawg dua lossis sib npaug rau 0.035 |
Tensile Strength (Rm): Ntau dua los yog sib npaug rau 785MPa, Tawm Zog (ReL/Rr0.2): Ntau dua lossis sib npaug li 500MPa, Elongation (A): Ntau dua lossis sib npaug li 9%, Thaj Chaw Txo Rate (Z): Ntau dua lossis sib npaug li 20%, Hardness (HBW10/3000): HBW227-388, Txias Khoov (d=3a): 30 degree tsis muaj tawg |
| 12kg ua |
55# |
C: {{0}}.52-0.60, Mn: 0.50-0.80, Si: 0. 17-0.37, S: Tsawg dua lossis sib npaug rau 0.035, P: Tsawg dua lossis sib npaug rau 0.035 |
Tensile Strength (Rm): Ntau dua los yog sib npaug rau 785MPa, Tawm Zog (ReL/Rr0.2): Ntau dua lossis sib npaug li 500MPa, Elongation (A): Ntau dua lossis sib npaug li 9%, Thaj Chaw Txo Rate (Z): Ntau dua lossis sib npaug li 20%, Hardness (HBW10/3000): HBW227-388, Txias Khoov (d=3a): 30 degree tsis muaj tawg |
| 24kg ua |
55# |
C: {{0}}.52-0.60, Mn: 0.50-0.80, Si: 0. 17-0.37, S: Tsawg dua lossis sib npaug rau 0.035, P: Tsawg dua lossis sib npaug rau 0.035 |
Tensile Strength (Rm): Ntau dua los yog sib npaug rau 785MPa, Tawm Zog (ReL/Rr0.2): Ntau dua lossis sib npaug li 500MPa, Elongation (A): Ntau dua lossis sib npaug li 9%, Thaj Chaw Txo Rate (Z): Ntau dua lossis sib npaug li 20%, Hardness (HBW10/3000): HBW227-388, Txias Khoov (d=3a): 30 degree tsis muaj tawg |
| 43kg ua |
55# |
C: {{0}}.52-0.60, Mn: 0.50-0.80, Si: 0. 17-0.37, S: Tsawg dua lossis sib npaug rau 0.035, P: Tsawg dua lossis sib npaug rau 0.035 |
Tensile Strength (Rm): Ntau dua los yog sib npaug rau 785MPa, Tawm Zog (ReL/Rr0.2): Ntau dua lossis sib npaug li 500MPa, Elongation (A): Ntau dua lossis sib npaug li 9%, Thaj Chaw Txo Rate (Z): Ntau dua lossis sib npaug li 20%, Hardness (HBW10/3000): HBW227-388, Txias Khoov (d=3a): 30 degree tsis muaj tawg |
| 50kg ua |
55# |
C: {{0}}.52-0.60, Mn: 0.50-0.80, Si: 0. 17-0.37, S: Tsawg dua lossis sib npaug rau 0.035, P: Tsawg dua lossis sib npaug rau 0.035 |
Tensile Strength (Rm): Ntau dua los yog sib npaug rau 785MPa, Tawm Zog (ReL/Rr0.2): Ntau dua lossis sib npaug li 500MPa, Elongation (A): Ntau dua lossis sib npaug li 9%, Thaj Chaw Txo Rate (Z): Ntau dua lossis sib npaug li 20%, Hardness (HBW10/3000): HBW227-388, Txias Khoov (d=3a): 30 degree tsis muaj tawg |
| 60kg ua |
55# |
C: {{0}}.52-0.60, Mn: 0.50-0.80, Si: 0. 17-0.37, S: Tsawg dua lossis sib npaug rau 0.035, P: Tsawg dua lossis sib npaug rau 0.035 |
Tensile Strength (Rm): Ntau dua los yog sib npaug rau 785MPa, Tawm Zog (ReL/Rr0.2): Ntau dua lossis sib npaug li 500MPa, Elongation (A): Ntau dua lossis sib npaug li 9%, Thaj Chaw Txo Rate (Z): Ntau dua lossis sib npaug li 20%, Hardness (HBW10/3000): HBW227-388, Txias Khoov (d=3a): 30 degree tsis muaj tawg |
| 75kg ua |
55# |
C: {{0}}.52-0.60, Mn: 0.50-0.80, Si: 0. 17-0.37, S: Tsawg dua lossis sib npaug rau 0.035, P: Tsawg dua lossis sib npaug rau 0.035 |
Tensile Strength (Rm): Ntau dua los yog sib npaug rau 785MPa, Tawm Zog (ReL/Rr0.2): Ntau dua lossis sib npaug li 500MPa, Elongation (A): Ntau dua lossis sib npaug li 9%, Thaj Chaw Txo Rate (Z): Ntau dua lossis sib npaug li 20%, Hardness (HBW10/3000): HBW227-388, Txias Khoov (d=3a): 30 degree tsis muaj tawg |